Effects of two-step high-energy ball milling process and hot isostatic pressing on the mechanical properties of PM magnesium

Jesus María Rios, Alex Humberto Restrepo, Alejandro Alberto Zuleta, Francisco Javier Bolívar, Juan Guillermo Castaño, Esteban Correa, Félix Echeverria

Resultado de la investigación: Contribución a una revistaArtículorevisión exhaustiva

Resumen

Commercial powders of magnesium were processed by high-energy ball milling (HEBM) using a two-stage composite process. The microstructural and morphological evolution of the powders was studied using scanning electron microscopy (SEM), energy-dispersive spectrometry (EDX), and X-ray diffraction (XRD). From the results obtained, it was determined that the energy transferred by means of the control of balls size and high milling speeds allowed the particles of Mg powder to deform and fracture, achieving grain refinement and particle size reduction in a relatively short time. Likewise, milling energy calculations were made to determine the effect of the milling parameters. Subsequently, milled powders were compacted and HIPed reaching a densification of 95%. Finally, mechanical tests showed that the developed process increased the hardness and compressive strength of Mg compared to the material obtained by casting.

Idioma originalInglés
Páginas (desde-hasta)187-196
Número de páginas10
PublicaciónInternational Journal of Advanced Manufacturing Technology
Volumen121
N.º1-2
DOI
EstadoAceptada/en prensa - 2022

Huella

Profundice en los temas de investigación de 'Effects of two-step high-energy ball milling process and hot isostatic pressing on the mechanical properties of PM magnesium'. En conjunto forman una huella única.

Citar esto